Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | | <0.10 % |
| Shrinkage rate | | DIN 16901 | 0.30to0.70 % |
| density | | ISO 1183 | 1.61 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2 | 180 MPa |
| Tensile strain | Yield | ISO 527-2 | 2.0 % |
| Flexural modulus | | ISO 178 | 11000 MPa |
| bending strength | | ISO 178 | 250 MPa |
| Bending Strain | | ISO 178 | 2.5 % |
| Tensile modulus | | ISO 527-2 | 13000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1fU | 28 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| insulation resistance | | IEC 60167 | >1.0E+12 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | UL 746B | 250 °C |
| maximum service temperature | | | 280 °C |
| vicat | | ISO 306/A | 325 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.