PA6 A1022GFL UNITIKA JAPAN

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedenhanceFiller: Glass fiber reinf15% filler by weight

Typical Applications:

Engine hood partsConstruction application fieldAutomotive sectorcontainerElectrical enclosureApplication in the automotive fieldParts under the hood of a carArchitectural application fieldVehicle electronics

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Engine hood parts \| Construction application field \| Automotive sector \| container \| Electrical enclosure \| Application in the automotive field \| Parts under the hood of a car \| Architectural application field \| Vehicle electronics
Properties:	Glass fiber reinforced \| enhance \| Filler: Glass fiber reinf \| 15% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		kJ/m²	23	33
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.9mm		HB	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength			175	MPa
Tensile modulus		MPa	5600	3000
tensile strength	Break	MPa	120	70.0
Tensile strain	Break	%	2.7	4.6
Bending modulus		MPa	5000	2800
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	°C	214	--
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	190	--
Linear coefficient of thermal expansion	MD	cm/cm/°C	4.2E-05	4.2E-05
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:3.20mm	%	0.80-1.0	0.80到1.0
Shrinkage rate	Shrinkage rate	MD:3.20mm	%	0.30-0.50	0.30到0.50
Water absorption rate	23°C,24hr	%	1.5	1.5
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	%	2.4	2.4
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ohms·cm	2E+15	8E+13
Dielectric strength	1.00mm	kV/mm	39
Dielectric constant	1MHz		3.30	--
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale		116	103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.