Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTM D792 | 0.621 cm³/g |
| Shrinkage rate | | 内部方法 | 0.30-0.40 % |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| Shrinkage rate | | 内部方法 | 0.60-0.80 % |
| Water absorption rate | | ASTM D570 | 0.070 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 109 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 75.8 Mpa |
| Flexural modulus | | ASTM D790 | 8270 Mpa |
| bending strength | | ASTM D790 | 124 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1.3E+15 ohms·cm |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 |
| dielectric strength | | ASTM D149 | 30 KV/mm |
| dielectric strength | | ASTM D149 | 24 KV/mm |
| dielectric constant | | ASTM D150 | 4.30 |
| dielectric constant | | ASTM D150 | 4.00 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Dissipation Factor | | ASTM D150 | 0.020 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 216 °C |
| Heat distortion temperature | | ASTM D648 | 199 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 2.5E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Imp | | UL 746 | 140 °C |
| RTI Str | | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.