Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.37 g/cm³ |
| Water absorption rate | | ISO 62 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 120 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | >4.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2 | 125 MPa |
| Tensile strain | Break | ISO 527-2 | >50 % |
| Flexural modulus | | ISO 178 | 3500 MPa |
| compression stress | | ISO 604 | 56.0 MPa |
| compression stress | | ISO 604 | 88.0 MPa |
| compression stress | | ISO 604 | 95.0 MPa |
| coefficient of friction | Steel - Dynamic | ASTM D1894 | 0.020to0.080 |
| coefficient of friction | Steel - Static | ASTM D1894 | 0.24to0.28 |
| tensile strength | Yield | ISO 527-2 | 74.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 5E+12 ohms |
| dielectric strength | | IEC 60243-1 | 90 kV/mm |
| dielectric constant | | IEC 60250 | 3.60 |
| Dissipation Factor | | IEC 60250 | 0.019 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 74.0 °C |
| melting temperature | | ISO 3146 | 255 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1050 J/kg/°C |
| thermal conductivity | | ISO 8302 | 0.21 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.