HIPS VE-1897 BK Samsung Cheil South Korea

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanFlame retardant

Typical Applications:

Home appliance componentsTV casingDisplay frameLCD TV

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| TV casing \| Display frame \| LCD TV
Properties:	High temperature resistan \| Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2060	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2090	Mpa
tensile strength	Yield	ASTM D638	22.6	Mpa
	tensile strength	Yield	ISO 527-2/50	23.0	Mpa
		tensile strength	Break	ASTM D638	25.5	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	22.0	Mpa
elongation	Break	ASTM D638	35	%
Tensile strain	Break	ISO 527-2/50	35	%
Bending modulus		ASTM D790	1910	Mpa
Bending modulus	Bending modulus		ISO 178	1600	Mpa
bending strength		ASTM D790	31.4	Mpa
bending strength	bending strength		ISO 178	37.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	79.0	°C
Vicat softening temperature	--	ISO 306/B50	81.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	85.0	°C
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	81.0	°C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	84.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	75.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	70.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200°C/5.0kg	ASTM D1238	16	g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	16	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30-0.40	%
	Shrinkage rate	TD：3.20mm	ASTM D955	0.40-0.50	%
	Shrinkage rate	Shrinkage rate	MD：3.20mm	ISO 2577	0.30-0.40	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	100
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	98

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.