PC GZ-2510 IDEMITSU JAPAN

114

Form：Granules | Grade：Extrusion grade

Properties:

Glass fiber reinforcedBromine freeFlame retardantGlass fiber reinforced maFiller: Glass fiber reinfPhosphorus contentLow (to none)Bromine freeFlame retardant performan10%Filler by weight10%Filler by weight

Typical Applications:

Industrial applicationsFitness equipmentPrinting machine partsLCD applicationLCD applicationPower/Other ToolsmodelPrinting machine parts

Supplier(2)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Industrial applications \| Fitness equipment \| Printing machine parts \| LCD application \| LCD application \| Power/Other Tools \| model \| Printing machine parts
Properties:	Glass fiber reinforced \| Bromine free \| Flame retardant \| Glass fiber reinforced ma \| Filler: Glass fiber reinf \| Phosphorus content \| Low (to none) \| Bromine free \| Flame retardant performan \| 10% \| Filler by weight \| 10% \| Filler by weight

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	8.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	120	Mpa
Bending modulus		ISO 178	3500	Mpa
Nominal tensile fracture strain		ISO 527-2	5.0	%
tensile strength	Yield	ISO 527-2	80.0	Mpa
Charpy Notched Impact Strength		ISO 179	8	kJ/m²
bending strength		ISO 178	120	Mpa
Bending modulus		ISO 178	3500	Mpa
Tensile strain	Break	ISO 527-2	5	%
tensile strength	Break	ISO 527-2	80	Mpa
Rockwell hardness	M -Sale	ISO 2039-2	65
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.50 mm	UL 94	V-0
Linear coefficient of thermal expansion		ASTM D696	0.000045	cm/cm/℃
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	142	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	142	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	4.5E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	Internal Method	0.6	%
density		ISO 1183	1.27	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Shrinkage rate	MD:2.00mm	Internal Method	0.40	%
Spiral flow length		Internal Method	21.0	CM
density		ISO 1183	1.27	g/cm³
Water absorption rate	Equilibrium, 23℃, 50% RH	ISO 62	0.15	%
Shrinkage rate	MD: 2.00 mm	Internal Method	0.4	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	Internal Method	0.60	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	> 22	KV/mm
Arc resistance		ASTM D495	110	sec
Dielectric constant	1 MHz	IEC 60250	2.95
Volume resistivity		ASTM D257	>1.0E+16	ohms·cm
Dielectric strength		IEC 60243-1	>22	KV/mm
Dielectric constant	1MHz	IEC 60250	2.95
Dissipation factor	1MHz	IEC 60250	9E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	65
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut			>PC-GF10<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC GZ-2510 IDEMITSU JAPAN

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index