ABS H801 INEOS USA

Form：Granules | Grade：Heat resistant grade

Properties:

UV resistanceheat-resisting

Typical Applications:

Home appliance componentsAutomotive sectorAutomotive interior partsApplication in the automotive fieldAutomotive interior equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Automotive sector \| Automotive interior parts \| Application in the automotive field \| Automotive interior equipment
Properties:	UV resistance \| heat-resisting

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 294	240	°C
Injection speed		ISO 294	240	mm/sec
Burning rate		ISO 3795	45	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ISO 178	2300	Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	60	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12	kJ/m²
bending strength	23°C	ISO 178	77	Mpa
Tensile modulus	23°C	ISO 527-2	2400	Mpa
Elongation at Break	23°C	ISO 527-2	>=15	%
Elongation at Break	Elongation at Break	Yield，23°C	ISO 527-2	3	%
tensile strength	Yield，23°C	ISO 527-2	49	Mpa
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	12	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	30	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	160	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	220	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05	cm/cm/°C
Vicat softening temperature	5.10kg	ISO 306/A50	105	°C
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	99	°C
Hot deformation temperature	Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	106	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	线性收缩率	ISO 294-4	0.5-0.7	%
melt mass-flow rate	melt mass-flow rate	220℃/10.0Kg	ISO 1133	9	g/10min
density		ISO 1183	1.07	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	相对漏电起痕指数	IEC 60112	600	V
	Dissipation factor		IEC 60250	0.09
	Dissipation factor	Dissipation factor		IEC 60250	0.05
Dielectric constant		IEC 60250	3.1	100HZ
Dielectric constant	Dielectric constant		IEC 60250	3	1MHz
Dielectric strength	1.00mm	IEC 60243-1	38	KV/mm
Surface resistivity		IEC 60093	1E+16	Ω.cm
Volume resistivity		IEC 60093	1E+14	Ω.cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	105	Mpa
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
Ignition temperature of heating wire	2.00mm	IEC 60695-2-12	700	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.