POM 500T NC010 DUPONT NETHERLANDS

Form：Granules | Grade：Injection grade

Properties:

High rigiditywear resistantThermal stability

Typical Applications:

Automotive Applicationsfibre

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| fibre
Properties:	High rigidity \| wear resistant \| Thermal stability

Certificates

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Pressure range			80-100	Mpa
Melting temperature range			210-220	°C
Mold temperature range			80-100	°C
water content			＜0.2	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile stress	Yield	ISO 527-1/-2	71	Mpa
Tensile strain	Yield	ISO 527-1/-2	14	%
elongation	Break	ISO 527-1/-2	20	%
Tensile modulus		ISO 527-1/-2	3300	Mpa
Bending modulus		ISO 178	3000	Mpa
Impact strength of cantilever beam gap	-40℃	ISO 180/1A	6	kJ/㎡
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ISO 180/1A	6	kJ/㎡
Charpy Notched Impact Strength		ISO 179/leA	5	kJ/㎡
Impact strength of simply supported beam without notch		ISO 179/leU	160	kJ/㎡
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa	ISO 75-1/-2	165	°C
Hot deformation temperature	Hot deformation temperature	1.80MPa	ISO 75-1/-2	104	°C
Melting temperature	10℃/min	ISO 3146℃	178	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.43	g/cm³
Water absorption rate		ISO 62	0.17	%
Shrinkage rate	正常	ISO 294-4	1.9	%
Shrinkage rate	Shrinkage rate	平行		1.9	%
melt mass-flow rate	190℃，2.16kg	ISO 1133	14	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.