Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.923 g/cm³ |
| melt mass-flow rate | | ISO1133 | 2.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTMD2457 | >50 |
| gloss | | ASTMD2457 | >100 |
| Haze ratio | | ASTMD1003 | <8.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Blow-upRatio | | | 2.00到3.00 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 260 Mpa |
| Tensile stress | | ISO527-2 | 11.0 Mpa |
| | ISO8295 | >80 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Available film thickness | | | 20-100micron |
| Tensile stress | | ISO527-3 | 25.0 Mpa |
| Tensile stress | | ISO527-3 | 21.0 Mpa |
| elongation | | ISO527-3 | 250 % |
| elongation | | ISO527-3 | 600 % |
| Falling hammer impact | | ASTMD1709 | 110 g |
| Film thickness - tested | | | 50 µm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/A50 | 94.0 °C |
| | ISO3146 | 111 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.