PC/ABS CX7240 BK1D797 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh impact resistanceHigh mobility

Typical Applications:

Electrical fieldElectronic fieldArchitectural application fieldOutdoor applicationsEngine hood partsMedical suppliesNursing suppliesPlastic bagCastersAerospace ApplicationsLiquid handling

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Architectural application field \| Outdoor applications \| Engine hood parts \| Medical supplies \| Nursing supplies \| Plastic bag \| Casters \| Aerospace Applications \| Liquid handling
Properties:	Flame retardant \| High impact resistance \| High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	65.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.60 mm	UL 94	V-1
	UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94	5VB
Hot filament ignition temperature	1.5 mm13	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm13	IEC 60695-2-13	775	°C
UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	0.75 mm13	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.75 mm13	IEC 60695-2-13	775	°C
Hot filament ignition temperature	Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825	°C
Extreme Oxygen Index		ISO 4589-2	34	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span4	ASTM D790	104	Mpa
bending strength	bending strength	--5,6	ISO 178	96.0	Mpa
Bending modulus	--5	ISO 178	2500	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2500	Mpa
elongation	Break	ISO 527-2/50	90	%
	elongation	Break3	ASTM D638	100	%
		elongation	Yield	ISO 527-2/50	4.0	%
		elongation	elongation	Yield3	ASTM D638	4.1	%
tensile strength	Break	ISO 527-2/50	50.0	Mpa
	tensile strength	Break3	ASTM D638	58.0	Mpa
		tensile strength	Yield	ISO 527-2/50	65.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	65.0	Mpa
Tensile modulus	--	ISO 527-2/1	2600	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2600	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 90	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Spray nozzle temperature			250 to 300	°C
Processing (melt) temperature			250 to 300	°C
Mold temperature			60 to 85	°C
Exhaust hole depth			0.030 to 0.075	mm
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			230 to 280	°C
Temperature in the middle of the barrel			240 to 290	°C
Temperature at the front of the material cylinder			250 to 300	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ASTM D152511	110	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	93.0	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100	°C
Vicat softening temperature	--	ISO 306/B120	113	°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
RTI Elec		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI		UL 746	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.20	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60	%
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0	cm3/10min
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	18	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	35	KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	25	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Compared to the anti leakage trace index		UL 746	PLC 3
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.