Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 1.42 g/cm³ |
| Water absorption rate | | ASTMD570 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 80 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | | 1.669 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Hydrogen | | ASTMD1434 | 95 cm³·mm/m²/atm/24hr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ASTMD1894 | 0.31 |
| | ASTMD1894 | 0.33 |
| film | Test Condition | Test Method | Test Result |
|---|
| Water vapor permeability | | ASTME96 | 0.090 g·mm/m²/atm/24hr |
| CarbonDioxidePermeability | | ASTMD1434 | 5.1 cm³·mm/m²/atm/24hr |
| NitrogenPermeability | | ASTMD1434 | 1.8 cm³·mm/m²/atm/24hr |
| Secant modulus MD | | ASTMD882 | 2620 MPa |
| tensile strength | Yield | ASTMD882 | 62.1 MPa |
| tensile strength | Break | ASTMD882 | 75.8 MPa |
| elongation | Yield | ASTMD882 | 3.0 % |
| elongation | Break | ASTMD882 | <200 % |
| oxygen permeability | | ASTMD1434 | 13 cm³·mm/m²/atm/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 220 kV/mm |
| dielectric constant | | ASTMD150 | 2.84 |
| dielectric constant | | ASTMD150 | 2.82 |
| dielectric constant | | ASTMD150 | 2.80 |
| Dissipation Factor | | ASTMD150 | 4E-03 |
| Surface Resistivity | | ASTMD257 | 1E+16 ohms |
| Volume resistivity | | ASTMD257 | 1.2E+17 ohms·cm |
| Dissipation Factor | | ASTMD150 | 3E-03 |
| Dissipation Factor | | ASTMD150 | 2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | | 100 °C |
| melting temperature | | DSC | 380 °C |
| | TMA | 3.8E-05 cm/cm/°C |
| Service | | | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.