Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 1.5 % |
| Water absorption rate | | ISO62 | 0.50 % |
| density | | ISO1183 | 1.06 g/cm³ |
| Shrinkage rate | | ISO294-4 | 1.7 % |
| Shrinkage rate | | ISO294-4 | 1.8 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA12-HI,MHZ,16-010 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 1250 MPa |
| Tensile stress | Yield | ISO527-2 | 36.0 MPa |
| Tensile stress | Break | ISO527-2 | 33.0 MPa |
| Tensile strain | Yield | ISO527-2 | 8.0 % |
| Tensile strain | Break | ISO527-2 | 42 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 55 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+05 ohms·cm |
| insulation resistance | | IEC60167 | 1E+05 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO75-2/B | 130 °C |
| Heat Deflection Temperature | | ISO75-2/A | 50.0 °C |
| vicat | | ISO306/A | 175 °C |
| vicat | | ISO306/B | 140 °C |
| melting temperature | | ISO11357-3 | 178 °C |
| Linear thermal expansion coefficient | | ISO11359-2 | 1.8E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.