Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183/A | 1.50 g/cm³ |
| Water absorption rate | | ISO 62 | 0.24 % |
| Water absorption rate | | ISO 62 | 2.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 700 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 12400 MPa |
| bending strength | | ASTM D790 | 294 MPa |
| bending strength | | ISO 178 | 310 MPa |
| Tensile modulus | | ISO 527-2/1A | 16000 MPa |
| tensile strength | | ISO 527-2/1A | 200 MPa |
| Tensile strain | | ISO 527-2 | 3.6 % |
| Flexural modulus | | ASTM D790 | 11800 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 6.1E+16 ohms |
| Volume resistivity | | IEC 60093 | 2.6E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 26 kV/mm |
| relative permittivity | | IEC 60250 | 3.70 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 208 °C |
| melting temperature | | ISO 11357-3 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.