Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Melt volume flow rate | | ISO 1133 | 21.0 cm³/10min |
Shrinkage rate | | ISO 2577 | 0.70to0.90 % |
Shrinkage rate | | ISO 2577 | 0.10to0.20 % |
Shrinkage rate | | ISO 2577 | 0.70to0.90 % |
Shrinkage rate | | ISO 2577 | 0.10to0.20 % |
density | | ISO 1183 | 1.22 g/cm³ |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2/1 | 2000 MPa |
tensile strength | | ISO 527-2/50 | 55.0 MPa |
tensile strength | | ISO 527-2/50 | 45.0 MPa |
Tensile strain | | ISO 527-2/50 | 4.5 % |
Nominal tensile fracture strain | | ISO 527-2/50 | >50 % |
Flexural modulus | | ISO 178 | 2000 MPa |
bending strength | | ISO 178 | 65.0 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO 180/A | 45 kJ/m² |
Impact strength of cantilever beam gap | | ISO 180/A | 60 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | IEC 60093 | >1.0E+16 ohms·cm |
relative permittivity | | IEC 60250 | 3.20 |
relative permittivity | | IEC 60250 | 3.10 |
Dissipation Factor | | IEC 60250 | 3E-03 |
Dissipation Factor | | IEC 60250 | 0.015 |
Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/B | 100 °C |
Heat distortion temperature | | ISO 75-2/A | 75.0 °C |
vicat | | ISO 306/B120 | 122 °C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.