PA66 Vydyne® R535HT BK653

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.42 g/cm³
Shrinkage rate		ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.40 %
Water absorption rate		ISO 62	0.80 %
Water absorption rate	Water absorption rate		ISO 62	1.6 %

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	75 kJ/m²
Impact strength of cantilever beam gap		ISO 180	13 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	14 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	65 kJ/m²

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	11200 MPa
tensile strength	ISO 527-2	200 MPa
Tensile strain	ISO 527-2	3.2 %
Flexural modulus	ISO 178	10200 MPa
bending strength	ISO 178	280 MPa
Poisson's ratio	ISO 527	0.40

Thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature (HDT)		ISO 75-2/B	256 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/A	240 °C
melting temperature		ISO 11357-3	260 °C
		ISO 11359-2	1.9E-05 cm/cm/°C
			ISO 11359-2	8.1E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.