EPE ELITE™ 5401G
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.9175 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 1.0 g/10min | |
| 50.8 microns | |||
| 2500 ppm | |||
| 1000 ppm |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM2457 | 64 | |
| Haze ratio | ASTM D1003 | 13 ％ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| impact force | 18 ft-lbf/in3 | ||
| elongation | Break | ASTM D882 | 572 % |
| Break | ASTM D882 | 612 % | |
| Elmendorf tear strength | ASTM D192 | 780 g | |
| ASTM D192 | 975 g | ||
| Dart impact | ASTM D1709 | >=850 g | |
| tensile strength | ASTM D882 | 8.267 MPa | |
| ASTM D882 | 8.811 MPa | ||
| Secant modulus | ASTM D882 | 180.9 MPa | |
| ASTM D882 | 204.4 MPa | ||
| tensile strength | ASTM D882 | 38.04 MPa | |
| ASTM D882 | 36.54 MPa |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| impact force | ASTM D882 | 168 ft-lbf/in3 | |
| Puncture Resistance | 5.76 J | ||
| Elmendorf tear strength | ASTM D1922 | 15.4 g/micron | |
| ASTM D1922 | 19.19 g/micron | ||
| Starting temperature of heat sealing | 95.0 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM1525 | 100 °C | |
| Melting Temperature | 陶氏化学方法(DSC | 123 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.