PP TRANSMARE® 22CT20-0.001

Properties:
Filler
talc filler
20%
filler by volume
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183	1.04 g/cm³
melt mass-flow rate		ISO1133	20 g/10min

hardness	Test Condition	Test Method	Test Result
		ISO868	67

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2/1	2430 MPa
Tensile stress		ISO527-2/50	26.0 MPa
Tensile stress	Tensile stress		ISO527-2/50	24.0 MPa
TensileStrain		ISO527-2/50	3.1 %
Tensile strain		ISO527-2/50	8.0 %
Flexural modulus		ISO178	2550 MPa
Bending stress		ISO178	43.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO179/1U	55 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1U	28 kJ/m²
Impact strength of cantilever beam gap		ISO180/1A	2.3 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO180/1A	4.2 kJ/m²
Charpy Notched Impact Strength		ISO179/1A	2.1 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1A	3.8 kJ/m²
		ISO180/1U	20 kJ/m²
			ISO180/1U	43 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
vicat		ISO306/A	152 °C
Heat distortion temperature		ISO75-2/B	107 °C
Heat distortion temperature	Heat distortion temperature		ISO75-2/A	55.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.