Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.20 % |
| Shrinkage rate | | ASTM D955 | 0.60 % |
| Water absorption rate | | ASTM D570 | 1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 190 Mpa |
| elongation | | ASTM D638 | 3.0 % |
| Flexural modulus | | ASTM D790 | 17000 Mpa |
| bending strength | | ASTM D790 | 280 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1.0E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 18 KV/mm |
| dielectric constant | | ASTM D150 | 4.10 |
| Dissipation Factor | | ASTM D150 | 0.011 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 300 °C |
| Glass Transition Temperature | | | 95.0 °C |
| melting temperature | | | 320 °C |
| Linear coefficient of thermal expansion | | ASTM E831 | 1.8E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM E831 | 6.9E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.