Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| spiral flow length | | 内部方法 | 50.0 cm |
| Shrinkage rate | | ISO 294-4 | 0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Water absorption rate | | ISO 1110 | 1.2 % |
| density | | ISO 1183 | 1.62 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 280 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO 1172 | 50 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 17000 MPa |
| tensile strength | Break | ISO 527-2/5 | 210 MPa |
| Tensile strain | Break | ISO 527-2/5 | 2.2 % |
| Flexural modulus | | ISO 178 | 17500 MPa |
| bending strength | | ISO 178 | 320 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 215 °C |
| Heat distortion temperature | | ISO 75-2/C | 165 °C |
| melting temperature | | DIN EN11357-1 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.