Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.80 -- |
| Shrinkage rate | | % | 0.80 -- |
| Water absorption rate | | % | 1.5 -- |
| Water absorption rate | | % | 0.70 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | % | >50 ＞50 |
| Tensile modulus | | MPa | 1400 1100 |
| tensile strength | | MPa | 45.0 40.0 |
| tensile strength | | MPa | 60.0 50.0 |
| Tensile strain | | % | 10 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | -- 1E+13 |
| dielectric strength | | kV/mm | -- |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 115 -- |
| Heat distortion temperature | | °C | 45.0 -- |
| Continuous use temperature | | °C | 90.0to110 -- |
| Continuous use temperature | | °C | 150 -- |
| melting temperature | | °C | 178 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.2E-04 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.4E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.