| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 2.1 % |
| Shrinkage rate | | ISO 294-4 | 2.2 % |
| Water absorption rate | | ISO 62 | 8.5 % |
| Water absorption rate | | ISO 62 | 2.5 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2850 Mpa |
| Tensile stress | | ISO 527-2 | 85.0 Mpa |
| Tensile stress | | ISO 527-2 | 55.0 Mpa |
| Tensile strain | | ISO 527-2 | 5.0 % |
| Nominal tensile fracture strain | | ISO 527-2 | 40 % |
| Flexural modulus | | ISO 178 | 3000 Mpa |
| Bending stress | | ISO 178 | 80.0 Mpa |
| Poisson's ratio | | ISO 527-2 | 0.40 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| | | 280 到 295 °C |
| | | 280 到 295 °C |
| Temperature in Zone 3 of the material cylinder | | | 280 到 295 °C |
| | | 280 到 295 °C |
| Temperature in Zone 5 of the material cylinder | | | 280 到 295 °C |
| Melt Temperature | | | 270 到 295 °C |
| die temperature | | | 270 到 295 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+14 ohms·cm |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 60 到 75 °C |
| drying time | | | 4.0 hr |
| Suggested maximum moisture content | | | 0.050 到 0.10 % |
| Suggested maximum recycled material ratio | | | 25 % |
| Temperature at the rear of the barrel | | | 280 到 310 °C |
| Temperature in the middle of the barrel | | | 280 到 310 °C |
| Temperature at the front of the material cylinder | | | 280 到 310 °C |
| Spray nozzle temperature | | | 280 到 310 °C |
| Processing (melt) temperature | | | 285 到 305 °C |
| Temperature | | | 65 到 95 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 200 °C |
| Heat distortion temperature | | ISO 75-2/A | 65.0 °C |
| melting temperature | | ISO 11357-3 | 260 °C |
| | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| | ISO 11359-2 | 1.0E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.