Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.18 g/cm³ |
| Shrinkage rate | | | 0.90to1.2 % |
| Water absorption rate | | | 2.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 31 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 3500 MPa |
| Tensile modulus | | ISO 527-2 | 3800 MPa |
| tensile strength | Break | ISO 527-2 | 80.0 MPa |
| Tensile strain | Break | ISO 527-2 | 15 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 40 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 3146 | 220 °C |
| Heat distortion temperature | | ISO 75-2/B | 180 °C |
| Heat distortion temperature | | ISO 75-2/A | 70.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.