Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.36 -- |
| Shrinkage rate | | % | 0.90to1.2 -- |
| Water absorption rate | | % | 0.90to1.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 110 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 5500 2800 |
| tensile strength | | MPa | 75.0 50.0 |
| elongation | Break | % | 6.0 25 |
| Flexural modulus | | MPa | 5000 2000 |
| bending strength | | MPa | 120 70.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 50 100 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | kV/mm | 15 -- |
| Volume resistivity | | ohms·cm | 1E+12 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 170 -- |
| Heat distortion temperature | | °C | 120 -- |
| Continuous use temperature | | °C | 90.0to100 -- |
| melting temperature | | °C | 212to214 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare