Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Shrinkage rate | | ISO294-4 | 0.50 % |
| density | | ISO1183 | 1.19 g/cm³ |
| Melt volume flow rate | | ISO1133 | 15.0 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Limiting Oxygen Index | | ISO4589-2 | 29 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ElectrolyticalCorrosion-Step | | IEC60426 | A1 |
| Relative WeldLineStrength | | ISO527 | 60 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 5600 MPa |
| Tensile stress | Break | ISO527-2 | 110 MPa |
| Tensile strain | Break | ISO527-2 | 3.0 % |
| Flexural modulus | | ISO178 | 5700 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 50 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 50 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 33 kV/mm |
| | IEC60250 | 2.90 |
| | IEC60250 | 2.70 |
| Dissipation Factor | | IEC60250 | 8E-04 |
| Dissipation Factor | | IEC60250 | 1.8E-03 |
| CTI | | IEC60112 | 200 V |
| CTI | | IEC60112 | 175 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 190 °C |
| | ISO75-2/A | 185 °C |
| vicat | | ISO306/A | 200 °C |
| vicat | | ISO306/B | 190 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare