PP Homopolymer POLYfill PPH BK901213
0
- Properties:Fillermineral filler25%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.10 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 9.0 g/10min | |
| Shrinkage rate | ISO 294-4 | 1.1to1.3 % | |
| ISO 294-4 | 1.1to1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 2.0 kJ/m² | |
| ISO 179 | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Yield | ISO 527-2 | 8.0 % |
| Flexural modulus | ISO 178 | 2000 MPa | |
| bending strength | ISO 178 | 48.0 MPa | |
| tensile strength | ISO 527-2 | 20.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/B | 112 °C | |
| ISO 75-2/A | 62.0 °C | ||
| vicat | ISO 306/A50 | 145 °C | |
| ISO 306/B50 | 85.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.