Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.42 g/cm³ |
| melt mass-flow rate | | ISO1133 | 9.0 g/10min |
| Shrinkage rate | | ISO294-4 | 2.0 % |
| Water absorption rate | | ISO62 | 0.65 % |
| Water absorption rate | | ISO62 | 0.20 % |
| Melt volume flow rate | | ISO1133 | 7.00 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 140 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| burning rate | | FMVSS302 | <100 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISOType | | ISO1874 | POM-K,M-GNS,03-002 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2600 MPa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 10 % |
| Tensile strain | Break | ISO527-2/50 | 30 % |
| Flexural modulus | | ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 62.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 150 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 5.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 24 kV/mm |
| dielectric constant | | IEC60250 | 4.00 |
| Dissipation Factor | | IEC60250 | 9E-03 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| LimitTemperature-effect host operation | | | 100 °C |
| | ISO75-2/A | 110 °C |
| vicat | | ISO306/B | 150 °C |
| melting temperature | | ISO11357-3 | 167 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.