POM S9364

Form：Powder | Color：true qualities | Filler：Toughening agent 30 %

Properties:

High impact resistance

Typical Applications:

Bottle capEngine partsCar chargerGearsPulleyWasher

Supplier(0)

Product Description

Certificates(0)

Datasheet

Alternative Model(2)

Product Description

Typical Applications:	Bottle cap \| Engine parts \| Car charger \| Gears \| Pulley \| Washer
Properties:	High impact resistance
Color:	true qualities
Form:	Pellets
Filler:	Toughening agent 30%

Certificates

No Data...

Technical Data Sheet

冲击性能	Test Condition	Test Method	Test Result	Test Unit
无缺口伊佐德冲击强度	23°C	ISO 180/1U	无断裂
无缺口伊佐德冲击强度	无缺口伊佐德冲击强度	-30°C	ISO 180/1U	无断裂
悬壁梁缺口冲击强度	23°C	ISO 180/1A	20	kJ/m²
	悬壁梁缺口冲击强度	-30°C	ISO 180/1A	12	kJ/m²
	悬壁梁缺口冲击强度	悬壁梁缺口冲击强度	-40°C	ISO 180/1A	10	kJ/m²
简支梁无缺口冲击强度	23°C	ISO 179/1eU	无断裂
简支梁无缺口冲击强度	简支梁无缺口冲击强度	-30°C	ISO 179/1eU	无断裂
简支梁缺口冲击强度	23°C	ISO 179/1eA	21	kJ/m²
简支梁缺口冲击强度	简支梁缺口冲击强度	-30°C	ISO 179/1eA	11	kJ/m²
Mechanical Properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's ratio			0.43
弯曲应力(3.5%应变)		ISO 178	42.0	MPa
Flexural elasticity		ISO 178	1550	MPa
拉伸应变(屈服)		ISO 527-2/50	16%
拉伸应力(屈服)		ISO 527-2/50	43.0	MPa
Tensile modulus		ISO 527-1	1650	MPa
Thermal Properties	Test Condition	Test Method	Test Result	Test Unit
载荷下热变形温度	1.8MPa，未退火	ISO 75-2/A	75.0	°C
载荷下热变形温度	载荷下热变形温度	0.45MPa，未退火	ISO 75-2/B	140	°C
Physical Properties	Test Condition	Test Method	Test Result	Test Unit
Melt index			4	g/10min
moisture content	平衡，23℃，2.00mm，50% RH	ISO 62	0.25%
moisture content	moisture content	饱和，23℃，2.00mm	ISO 62	0.80%
Mold Shrinkage	流动	ISO 294-4	1.6%
Mold Shrinkage	Mold Shrinkage	垂直	ISO 294-4	1.5%
熔融体积流量(MVR)	190°C/2.16 kg	ISO 1133	4.0	cm³/10min
Solid specific gravity		ISO 1183	1.36	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.