POM TF-10LV TAIWAN POLYPLASTICS

Form：Granules | Grade：Injection grade

Properties:

High rigidityHigh temperature resistan

Typical Applications:

Automotive ApplicationsElectrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical applications
Properties:	High rigidity \| High temperature resistan

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	60.0	Mpa
Friction coefficient	Dynamic2	JISK7218	0.60
Friction coefficient	Friction coefficient	Steel - Dynamic3	JISK7218	0.30
Wear factor	0.49MPa,0.30m/sec4	JISK7218	<1.0	10^-8mm³/N·m
	Wear factor	0.49MPa,0.30m/sec5	JISK7218	100	10^-8mm³/N·m
		Wear factor	0.060MPa,0.15m/sec6	JISK7218	600	10^-8mm³/N·m
		Wear factor	Wear factor	0.060MPa,0.15m/sec7	JISK7218	700	10^-8mm³/N·m
Tensile modulus		ISO 527-2	1850	Mpa
tensile strength		ISO 527-2	46.0	Mpa
Nominal tensile fracture strain		ISO 527-2	55	%
Bending modulus		ISO 178	1700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	82.0	°C
Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	1.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	1.3E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.38	g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	10	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	9.00	cm3/10min
Shrinkage rate	TD:2.00mm	ISO 294-4	1.7	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	1.9	%
Water absorption rate	23°C,24hr	ISO 62	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	7E+12	ohms
Volume resistivity		IEC 60093	1E+13	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	65
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			CF2003/CF2004

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.