Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.90 % |
| Water absorption rate | | ISO 62 | 4.7 % |
| Water absorption rate | | ISO 62 | 1.5 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 105 |
| Rockwell hardness | | ISO 2039-2 | 125 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 27 mm/min |
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | HB |
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| FMVSS flammability | | FMVSS 302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 14000 Mpa |
| Tensile stress | | ISO 527-2 | 225 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Tensile creep modulus | | ISO 899-1 | -- Mpa |
| Tensile creep modulus | | ISO 899-1 | -- Mpa |
| Flexural modulus | | ISO 178 | 12000 Mpa |
| Bending stress | | ISO 178 | 340 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 85 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| | ISO 180/1U | 110 kJ/m² |
| | ISO 180/1U | 110 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Melt density | | | 1.29 g/cm³ |
| Ejection Temperature | | | 210 °C |
| Specific Heat Capacity of Melt | | | 2050 J/kg/°C |
| Thermal Conductivity of Melt | | | 0.25 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 62631-3-2 | -- ohms |
| Volume resistivity | | IEC 62631-3-1 | > 1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-1 | 27 KV/mm |
| | IEC 62631-2-1 | 4.10 |
| | IEC 62631-2-1 | 4.50 |
| Dissipation Factor | | IEC 62631-2-1 | 0.010 |
| Dissipation Factor | | IEC 62631-2-1 | 0.015 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 285 到 305 °C |
| Melt Temperature, Optimum | | | 295 °C |
| Temperature | | | 70 到 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 到 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 262 °C |
| | ISO 75-2/A | 255 °C |
| Glass transition temperature 3 | | ISO 11357-2 | 80.0 °C |
| vicat | | ISO 306/B50 | 255 °C |
| Melting temperature 3 | | ISO 11357-3 | 262 °C |
| | ISO 11359-2 | 1.5E-5 cm/cm/°C |
| | ISO 11359-2 | 2.0E-5 cm/cm/°C |
| | ISO 11359-2 | 9.0E-6 cm/cm/°C |
| | ISO 11359-2 | 7.9E-5 cm/cm/°C |
| | ISO 11359-2 | 6.1E-5 cm/cm/°C |
| | ISO 11359-2 | 1.3E-4 cm/cm/°C |
| Effective Thermal Diffusivity | | | 9.50E-8 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.