Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.2 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.65 % |
| Shrinkage rate | | ISO294-4 | 0.70 % |
| Water absorption rate | | ISO62 | 0.30 % |
| Water absorption rate | | ISO62 | 0.12 % |
| | ISO1133 | 19.0 cm3/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 116 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO489 | 1.58 °C |
| | ISO13468-2 | 89.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation at break | | ISO527-2 | >50 % |
| Tensile modulus | | ISO527-2 | 2400 Mpa |
| Tensile creep modulus | | ISO899-1 | 2200 Mpa |
| Tensile creep modulus | | ISO899-1 | 1900 Mpa |
| bending strength | | ISO178 | 98.0 Mpa |
| Flexural modulus | | ISO178 | 2350 Mpa |
| Charpy Notched Impact Strength | | ISO179/1eA | 65 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 75 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 12 kJ/m² |
| tensile strength | | ISO527-2 | 66.0 Mpa |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| fire rating | | ISO4589-2 | 27 % |
| fire rating | | UL-94 | 0.75mm V-2 |
| fire rating | | UL-94 | 1.50mm V-2 |
| fire rating | | UL-94 | 2.60mm V-2 |
| fire rating | | UL-94 | 2.70mm HB |
| fire rating | | UL-94 | 3.00mm HB |
| fire rating | | UL-94 | 6.00mm HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60093 | 1E+15 Ω.cm |
| Surface Resistivity | | IEC60093 | 1E+16 Ω.cm |
| Dielectric Strength | | IEC60243-1 | 25 KV/mm |
| dielectric constant | | IEC60250 | 3.00 1MHz |
| Dissipation Factor | | IEC60250 | 5E-04 100HZ |
| Dissipation Factor | | IEC60250 | 9E-03 1MHz |
| Dissipation Factor | | IEC60112 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/Bf | 136 °C |
| | ISO75-2/Af | 124 °C |
| vicat | | ISO306/B50 | 143 °C |
| | ISO11359-2 | 6.5E-05 cm/cm/°C |
| | ISO11359-2 | 6.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.