other	Test Condition	Test Method	Test Result	Test Unit
characteristic			高光泽高流动
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃,3.8kg	ASTM D-1238	7.9	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,1/8",5mm/min	ASTM D-638	46	Mpa
tensile strength	tensile strength	1/8",5mm/min，Break	ASTM D-638	44	Mpa
Elongation at Break	1/8",5mm/min	ASTM D-638	42	%
Impact strength of cantilever beam gap	23°C	ASTM D-256	30	kJ/m²
elongation at yield	1/8",5mm/min	ASTM D-638	3	%
Elongation at Break		ASTM D638/ISO 527	44	%
tensile strength		ASTM D638/ISO 527	46	kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	3	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	30	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	42	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	1/8",50℃/hr，120℃/10hr	ASTM D-1525	95	°C
Vicat softening temperature	Vicat softening temperature		ASTM D1525/ISO R306	95	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	7.9	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.