Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Apparent density | | ASTM D1895 | 1.00 g/cm³ |
Shrinkage rate | | ASTM D6289 | 0.15 % |
Water absorption rate | Equilibrium | ASTM D570 | 0.030 % |
density | | ASTM D792 | 2.09 g/cm³ |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638 | 23000 MPa |
tensile strength | | ASTM D638 | 65.0 MPa |
bending strength | | ASTM D790 | 114 MPa |
compressive strength | | ASTM D695 | 338 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Suspended wall beam without notch impact strength | | ASTM D256 | 21 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | ASTM D257 | 1E+13 ohms·cm |
dielectric strength | | ASTM D149 | 14 kV/mm |
dielectric strength | | ASTM D149 | 12 kV/mm |
dielectric constant | | ASTM D150 | 5.00 |
Dissipation Factor | | ASTM D150 | 0.015 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Glass Transition Temperature | | | 280 °C |
Linear coefficient of thermal expansion | | | 1.5E-05 cm/cm/°C |
Heat distortion temperature | | ASTM D648 | 204 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.