TPEE HTR8341C BK320 DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanChemical resistance

Typical Applications:

Automotive ApplicationsCableBlow molding applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Cable \| Blow molding applications
Properties:	High temperature resistan \| Chemical resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 8256/1	300	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	<100	mm/min
FMVSS flammability		FMVSS302	B
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength	横向Flow	ISO 34-1	120	kN/m
tear strength	tear strength	Flow	ISO 34-1	110	kN/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	300%Strain	ISO 527-2	23.0	Mpa
Tensile strain	Break	ISO 527-2	>300	%
Nominal tensile fracture strain		ISO 527-2	350	%
Bending modulus		ISO 178	80.0	Mpa
Tensile modulus		ISO 527-2	80.0	Mpa
tensile strength	Break	ISO 527-2	28.0	Mpa
	tensile strength	10%Strain	ISO 527-2	7.00	Mpa
		tensile strength	50%Strain	ISO 527-2	12.0	Mpa
		tensile strength	tensile strength	100%Strain	ISO 527-2	13.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
PeakCrystallizationTemperature		ISO 11357-3	167	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.7E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.3E-04	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	2E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	2.4E-04	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	5.44E-08	m²/s
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	56.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	42.0	°C
Brittle temperature		ISO 974	-100	°C
Glass transition temperature		ISO 11357-2	-70.0	°C
Melting temperature		ISO 11357-3	207	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ISO 1133	0.90	g/10min
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.50	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	9.5E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	4E+14	ohms
Volume resistivity		IEC 60093	8E+12	ohms·cm
Dielectric strength		IEC 60243-1	19	KV/mm
Dissipation factor	100Hz	IEC 60250	0.030
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD	ISO 868	40
Shore hardness	Shore hardness	ShoreD,15Sec	ISO 868	37

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.