PPO/PA NORYL GTX™ GTX675
113
- Properties:High mobilitydimensional stabilityHigh temperature resistanHydrolysis resistance
- Usages:Electrical applicationsIndustrial machinery
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 7.8 g/10min | |
| Melt volume flow rate | ISO 1133 | 7.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 1.3-1.5 % | |
| Water absorption rate | ISO 62 | 4.0 % | |
| ISO 62 | 0.40 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D638 | 6.1 % | |
| ISO 527-2/50 | 7.1 % | ||
| Flexural modulus | ASTM D790 | 2520 Mpa | |
| ISO 178 | 2470 Mpa | ||
| bending strength | ISO 178 | 103 Mpa | |
| ASTM D790 | 100 Mpa | ||
| Tensile modulus | ASTM D638 | 2420 Mpa | |
| ISO 527-2/1 | 2670 Mpa | ||
| tensile strength | ASTM D638 | 65.0 Mpa | |
| ISO 527-2/50 | 66.0 Mpa | ||
| ASTM D638 | 63.0 Mpa | ||
| ISO 527-2/50 | 64.0 Mpa | ||
| elongation | ASTM D638 | 3.8 % | |
| ISO 527-2/50 | 4.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 12 kJ/m² | |
| Dart impact | ASTM D3763 | 5.00 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | 内部方法 | 1.0E+3-1.0E+4 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ISO 11359-2 | 8.6E-05 cm/cm/°C | |
| Heat distortion temperature | ASTM D648 | 187 °C | |
| ISO 75-2/Bf | 184 °C | ||
| vicat | ASTMD152510 | 197 °C | |
| ISO 306/B120 | 198 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTME831 | 7.6E-05 cm/cm/°C | |
| ISO 11359-2 | 8.1E-05 cm/cm/°C | ||
| ASTME831 | 7.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.