Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.30 g/cm³ |
| Water absorption rate | | ASTMD570 | 0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 104 |
| Rockwell hardness | M-Scale | ASTMD785 | >125 |
| | ASTMD2240 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTMD2863 | 58 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Steel - Dynamic | | 0.16 |
| Steel - Static | | 0.15 |
| | | 0.16 |
| | | 0.18 |
| | | 0.14 |
| | | 0.16 |
| bending strength | | ASTMD790 | 221 MPa |
| Compression Modulus | | ASTMD695 | 5860 MPa |
| compressive strength | | ASTMD695 | 393 MPa |
| compressive strength | | ASTMD695 | 345 MPa |
| Tensile modulus | | ASTMD638 | 5860 MPa |
| tensile strength | | ASTMD638 | 159 MPa |
| elongation | Break | ASTMD638 | 3.0 % |
| Fatigue-%ofstresstofailure | | ASTMD638 | 35 % |
| Flexural modulus | | ASTMD790 | 6550 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 28 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 590 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 2E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 23 kV/mm |
| dielectric constant | | ASTMD150 | 3.40 |
| dielectric constant | | ASTMD150 | 3.40 |
| dielectric constant | | ASTMD150 | 3.30 |
| Dissipation Factor | | ASTMD150 | 0.0 |
| Dissipation Factor | | ASTMD150 | 3E-03 |
| Dissipation Factor | | ASTMD150 | 0.034 |
| arc resistance | | ASTMD495 | 185 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | TMA | 0.40 W/m/K |
| | ASTMD648 | 435 °C |
| Glass Transition Temperature | | DMA | 427 °C |
| | TMA | 2.3E-05 cm/cm/°C |
| | TMA | 3.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.