Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Density | | ISO 1183 | 1.51 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 6 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 1.7 % |
| Shrinkage rate | | ISO 294-4 | 2 % |
| Water absorption rate | | ISO 62 | 0.65 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A/1 | 2500 Mpa |
| tensile strength | | ISO 527-2/1A/50 | 48 Mpa |
| Tensile strain | | ISO 527-2/1A/50 | 7 % |
| Nominal tensile fracture strain | | ISO 527-2/1A/50 | 16 % |
| Tensile Creep Modulus（1 hr）? | | ISO 899-1 | 2100 Mpa |
| Tensile creep modulus | | ISO 899-1 | 1200 Mpa |
| Bending modulus | | ISO 178 | 2400 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap | | ISO 179/1eA | 4 kJ/m² |
| Impact strength of simply supported beam gap | | ISO 179/1eA | 4 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardant grade | | UL 94 | HB |
| Flame retardant grade | | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface resistivity | | IEC 60093 | 100000000000000 ohms |
| Volume resistivity | | IEC 60093 | 100000000000000 ohms·cm |
| dielectric strength | | IEC 60243-1 | 33 KV/mm |
| Relative permittivity | | IEC 60250 | 3.7 |
| Relative permittivity | | IEC 60250 | 3.7 |
| Dissipation Factor | | IEC 60250 | 0.002 |
| Dissipation Factor | | IEC 60250 | 0.008 |
| Compared to the leakage trace index | | IEC 60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 166 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 0.00011 1/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.