PC/ABS C7230P-7D7D002 SABIC INNOVATIVE NANSHA

Form：Granules

Properties:

Aging resistanceHigh mobility

Typical Applications:

Electronic and electrical accessoriesCastersHousehold appliances

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and electrical accessories \| Casters \| Household appliances
Properties:	Aging resistance \| High mobility

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 178	35	Mpa
	tensile strength	Type I, 50 mm/min，Yield	ASTM D638	45	Mpa
		tensile strength	Yield	ISO 178	55	Mpa
		tensile strength	tensile strength	Type I, 50 mm/min，Yield	ASTM D638	58	Mpa
Elongation at Break	Break	ISO 178	30	%
Elongation at Break	Elongation at Break	Type I, 50 mm/min，Break	ASTM D638	32	%
elongation at yield		ISO 178	3.8	%
elongation at yield	elongation at yield	Type I, 50 mm/min	ASTM D638	4	%
Tensile modulus		GB/T 15585-1995	5.2
Tensile modulus	Tensile modulus		1 mm/min; ISO 527	5.58
bending strength	1.3 mm/min, 50 mm span	ASTM D790	98	Mpa
bending strength	bending strength		2 mm/min; ISO 178	99	Mpa
Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	4.53
Bending modulus	Bending modulus		2 mm/min; ISO 178	4.58
Impact strength of cantilever beam gap		ASTM D256	0.69	J/cm
	Impact strength of cantilever beam gap		ASTM D256	0.55	J/cm
		Impact strength of cantilever beam gap			@Temperature -30.0
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		80104; ISO 180/1A	5	kJ/m²
Charpy Notched Impact Strength		Edgew 80104 sp=62mm; ISO 179/1eA	0.5	J/cm²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Flow	GB 1040	42	µm/m-°C
	Linear coefficient of thermal expansion	Flow	ISO 11359-2	42	µm/m-°C
		Linear coefficient of thermal expansion	Across Flow	GB 1040	49	µm/m-°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	59	µm/m-°C
Hot deformation temperature	1.8 MPa	Flatw 80104 sp=64mm; ISO 75/Af	89
Hot deformation temperature	Hot deformation temperature	1.8 MPa	ASTMF1249	88
Vicat softening temperature		Rate B/50; ISO 306	107
	Vicat softening temperature		Rate B/50; ASTM D1525	108
	Vicat softening temperature	Vicat softening temperature		Equate	110
UL flame retardant rating		UL 94	V-0
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		23°C / 50% RH; ISO 62	0.04	%
Water absorption rate	Water absorption rate	Saturation	ISO 62	0.09	%
Shrinkage rate	Flow	SABIC method	0.0025 - 0.0035	cm/cm
melt mass-flow rate		ASTM D1238	13
melt mass-flow rate	melt mass-flow rate		ASTM D1238	@Load 2.16 kg. Temperature 260
Compound melt index		MVR [cm^3/10 min]; ISO 1133	49.0 µm/m-°C	g/10 min
Compound melt index	Compound melt index			@Load 2.16 kg. Temperature 260

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.