PS Luranyl® KR 2462 G2 ROMIRA GERMANY

Properties:

Filler glass fiber reinforced material 10% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 10% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.60mm	UL 94	V-0
Hot filament ignition temperature	2.00mm	IEC 60695-2-13	775	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1	3800	MPa
tensile strength	Yield,23°C	ISO 527-2/5	82.0	MPa
Tensile strain	Break,23°C	ISO 527-2/5	4.0	%
bending strength	23°C	ISO 178	120	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity		DIN 52612	0.21	W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	135	°C
Vicat softening temperature		ISO 306/B50	150	°C
Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	4.0E-5到5.0E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	23°C,3.20mm	ISO 294-4	0.40to0.50	%
Water absorption rate	23°C,24hr	ISO 62	<0.15	%
density		ISO 1183	1.15	g/cm³
Melt Volume Flow Rate (MVR)	250°C/21.6kg	ISO 1133	15.0	cm³/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.