PA12 EOS PA 2200 Top Speed 1.0 EOS GmbH
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 内部方法 | 0.930 g/cm³ | |
| thickness | 180.0 µm |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 75 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 4.4 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 4.8 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 53 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1500 MPa | |
| tensile strength | ISO 527-2 | 45.0 MPa | |
| ISO 527-2 | 38.0 MPa | ||
| Tensile strain | ISO 527-2 | 3.0 % | |
| ISO 527-2 | 18 % | ||
| Flexural modulus | ISO 178 | 1500 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B50 | 163 °C | |
| melting temperature | ISO 11357 | 176 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.