Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.24 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 6.0to10 g/10min |
| Shrinkage rate | | ISO 294-4 | 0.72 % |
| Shrinkage rate | | ISO 294-4 | 0.68 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 68.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 5.7 % |
| Flexural modulus | | ISO 178 | 2480 MPa |
| bending strength | | ISO 178 | 105 MPa |
| Tensile modulus | | ISO 527-2 | 2600 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/A | 5.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Dissipation Factor | | IEC 60250 | 8E-04 |
| Dissipation Factor | | IEC 60250 | 6.4E-03 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 40 kV/mm |
| dielectric constant | | IEC 60250 | 3.10 |
| dielectric constant | | IEC 60250 | 3.10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 170 °C |
| Glass Transition Temperature | | ISO 11357-2 | 185 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.