other	Test Condition	Test Method	Test Result	Test Unit
characteristic			耐热性高无卤
purpose			电气电子应用领域
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180	13	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.2mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	2500	Mpa
tensile strength	Yield	ISO 527-2/50	62.0	Mpa
Tensile strain	Break	ISO 527-2/50	>20	%
Bending modulus		ISO 178	2600	Mpa
bending strength		ISO 178	93.0	Mpa
Rockwell hardness		ASTM D785	113
Bending modulus		ASTM D790/ISO 178	2650	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	93.2	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	91.0	°C
Vicat softening temperature		ISO 306/B50	99.0	°C
Hot deformation temperature	HDT	ASTM D648/ISO 75	103	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	250°C/2.16kg	ISO 1133	20	g/10min
Shrinkage rate	MD	Internal Method	0.40-0.60	%
density		ASTM D792/ISO 1183	1.19

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.