HIPS 622N
0
- Properties:High impact resistancegood fluidityand high heat resistance
- Usages:Furnituretoysdisposable alcoholic beveragesfood packagingdisposable tableware
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.04 g/cm3 | |
| Melt volume flow rate | ISO 1133 | 4.80 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.50-0.70 % | |
| Water absorption rate | ISO 62 | <0.10 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ISO 527-2/50 | 26.0 MPa |
| Break | 25.0 | ||
| Tensile strain | Yield | ISO 527-2/50 | 1.8 % |
| elongation at break | ISO 527-2/50 | 50 % | |
| bending strength | ISO 178 | 42.0 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 10 kJ/m2 | |
| ball-indentation hardness | ISO 2039-1 | 80.0 MPa | |
| Tensile modulus | ISO 527-2 | 1800 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 82.0 ℃ | |
| vicat | ISO 306/B50 | 89.0 ℃ | |
| Linear coefficient of thermal expansion | DIN 53752 | 0.000080 cm/cm./℃ | |
| thermal conductivity | DIN 42612 | 0.16 W/m/k |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.