PC/PET X8300CL GN9C021T SABIC EU

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh heat resistance

Typical Applications:

Automotive ApplicationsElectronic and electrical accessories

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electronic and electrical accessories
Properties:	Flame retardant \| High heat resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ISO 489	1.539
transmissivity	2540 μm	ASTM D1003	88.0	%
turbidity	2540 μm	ASTM D1003	1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	95.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0 mm	UL 94	V-2
Burning wire flammability index	1.0 mm	IEC 60695-2-12	750	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	1520	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	1600	Mpa
tensile strength	Yield3	ASTM D638	47.0	Mpa
	tensile strength	Yield	ISO 527-2/50	55.0	Mpa
		tensile strength	Break3	ASTM D638	46.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	54.0	Mpa
elongation	Yield3	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	> 5.0	%
		elongation	Break3	ASTM D638	150	%
		elongation	elongation	Break	ISO 527-2/50	> 200	%
Bending modulus	50.0 mm Span4	ASTM D790	1680	Mpa
Bending modulus	Bending modulus	--5	ISO 178	1700	Mpa
bending strength	--5,6	ISO 178	78.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	71.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			65 to 75	°C
drying time			3.0 to 5.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 80	%
Temperature at the rear of the barrel			240 to 250	°C
Temperature in the middle of the barrel			240 to 260	°C
Temperature at the front of the material cylinder			245 to 265	°C
Spray nozzle temperature			245 to 265	°C
Processing (melt) temperature			245 to 265	°C
Mold temperature			45 to 60	°C
Back pressure			0.200 to 0.500	Mpa
Screw speed			20 to 100	rpm
Exhaust hole depth			0.013 to 0.020	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	79.0	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	75.0	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	80.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	78.0	°C
Vicat softening temperature	--	ASTM D152510	91.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	96.0	°C
Ball Pressure Test	85°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	1.1E-4	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 60°C	ISO 11359-2	9.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	1.1E-4	cm/cm/°C
			Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	1.1E-4	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 60°C	ISO 11359-2	9.0E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.23	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	265°C/2.16 kg	ASTM D1238	15	g/10 min
Melt Volume Flow Rate (MVR)	265°C/2.16 kg	ISO 1133	15.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.80	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.60	%
Water absorption rate	Saturation, 23°C	ISO 62	0.050	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	> 1.0E+15	ohms
Volume resistivity		ASTM D257	> 1.0E+15	ohms·cm
Compared to the anti leakage trace index		UL 746	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	Shore D, 10 Sec	ASTM D2240	73

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.