Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1475 | 1.05 g/cm³ |
| Specific volume | | ASTMD1475 | 0.954 cm³/g |
| Shrinkage rate | | ASTMD2566 | 0.70 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| STORAGE STABILITY | | | 10到20 min |
| Thermosetting mixed viscosity | | ASTMD2393 | 80.0 cP |
| stripping time | | | 120到480 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore Hardness | | ASTMD2240 | 70 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Mixing Ratio | | | 1A:1Bbyvolume100A:90Bbyweight |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 924 MPa |
| tensile strength | | ASTMD638 | 20.7 MPa |
| elongation | Break | ASTMD638 | 8.0 % |
| Flexural modulus | | ASTMD790 | 758 MPa |
| bending strength | | ASTMD790 | 24.1 MPa |
| Compressive Modulus | | ASTMD695 | 278 MPa |
| compressive strength | | ASTMD695 | 24.5 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ASTMD648 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.