Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.25 g/cm³ |
| Water absorption rate | | ASTMD570 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTMD638 | 100 MPa |
| elongation | Break | ASTMD638 | 3.5 % |
| Flexural modulus | | ASTMD790 | 4400 MPa |
| bending strength | | ISO 178 | 140 MPa |
| bending strength | Break | ASTM D790 | 140 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| dielectric strength | | ASTMD149 | 32 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 250 °C |
| melting temperature | | ASTMD2117 | 260 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3E-05 cm/cm/°C |
| Heat distortion temperature | | ASTMD648 | 255 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.