| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 表观密度 | | JISK6891 | 1.00到1.40 g/cm³ |
| 熔体质量流动速率 | 372°C/5.0kg | ASTMD1238 | 10到17 g/10min |
| 吸水率 | 饱和 | ASTMD570 | <0.010 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 熔融温度 | | ASTMD4591 | 300到310 °C |
| 线性热膨胀系数 | MD：20到100°C | ASTMD696 | 1.2E-04 cm/cm/°C |
| 比热 | | | 1050 J/kg/°C |
| 导热系数 | | ASTMC177 | 0.26 W/m/K |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 1.6mm | UL94 | V-0 |
| 极限氧指数 | 1.57mm | ASTMD2863 | >95 % |
| 充模分析 | Test Condition | Test Method | Test Result |
|---|
| 熔体粘度 | 380°C | | 2.00E+6到2.50E+7 mPa·s |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 负载变形 | 25°C,14MPa3 | ASTMD621 | 8.00到9.00 % |
| 负载变形 | 100°C,6.9MPa2 | ASTMD621 | 2.00到3.00 % |
| 负载变形 | 100°C,6.9MPa3 | ASTMD621 | 8.50到9.50 % |
| FlexuralStrength | | ASTMD790 | Nobreak |
| 抗张强度 | 屈服 | JISK6891 | 25.4到30.4 Mpa |
| 伸长率 | 断裂 | JISK6891 | 350到450 % |
| 弯曲模量 | | ASTMD790 | 580到690 Mpa |
| 压缩模量 | | ASTMD695 | 490到590 Mpa |
| 压缩强度 | 1%应变 | ASTMD695 | 4.90到5.90 Mpa |
| 压缩强度 | 25%应变 | ASTMD695 | 31.4到33.3 Mpa |
| 压缩强度 | 摩擦系数(与钢-静态) | ASTMD695 | 0.040到0.050 |
| 负载变形 | 25°C,14MPa2 | ASTMD621 | 2.50到3.00 % |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 肖氏硬度 | 邵氏D | ASTMD2240 | 60到70 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.