PA66 A3GF33 AKRO-PLASTIC GERMANY

Form：Granules | Grade：Injection grade

Properties:

Filler: Glass fiber reinf33% filler by weight

Typical Applications:

Machine/mechanical componentsEngineering accessoriesApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Machine/mechanical components \| Engineering accessories \| Application in the automotive field
Properties:	Filler: Glass fiber reinf \| 33% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Burning rate	1.00mm	FMVSS302	<100	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break	ISO 527-2/5	3.0	%
tensile strength	Break	ISO 527-2/5	210	Mpa
Tensile modulus		ISO 527-2/1	11500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	255	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260	°C
Melting temperature		DIN EN11357-1	262	°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	220	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Hygroscopicity	70°C，62%RH	ISO 1110	1.8to2.0	%
Water absorption rate	Saturation,23°C	ISO 62	4.7to5.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Volume resistivity		IEC 60093	1E+13	ohms·cm
Surface resistivity		IEC 60093	1E+12	ohms
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ReinforcementContent		ISO 1172	33	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.