PBT+PET SCHULADUR® A1 GF 30 HF FR 1

Properties:
Filler
glass fiber reinforced material
30%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183/A	1.68 g/cm³
Melt volume flow rate		ISO 1133	54.0 cm³/10min

flammability	Test Condition	Test Method	Test Result
burning rate		ISO 3795	0.0 mm/min
Hot filament ignition temperature		IEC 60695-2-13	675 °C
Hot filament ignition temperature	Hot filament ignition temperature		IEC 60695-2-13	675 °C
Limiting Oxygen Index		ISO 4589-2	34 %
burning rate		ISO 3795	0.0 mm/min
burning rate	burning rate		ISO 3795	0.0 mm/min
UL flame retardant rating		UL 94	V-0
	UL flame retardant rating		UL 94	V-0
		UL flame retardant rating		UL 94	V-0
			UL flame retardant rating		IEC 60695-11-10,-20	V-0
				UL flame retardant rating		IEC 60695-11-10,-20	V-0
				UL flame retardant rating	UL flame retardant rating		IEC 60695-11-10,-20	V-0
Burning wire flammability index		IEC 60695-2-12	960 °C
	Burning wire flammability index		IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index		IEC 60695-2-12	960 °C
Hot filament ignition temperature		IEC 60695-2-13	675 °C

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	7.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	46 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	7.0 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1A/1	12000 MPa
tensile strength	Break	ISO 527-2/1A/5	148 MPa
Tensile strain	Break	ISO 527-2/1A/5	2.0 %

Electrical performance	Test Method	Test Result
Surface Resistivity	IEC 60093	>1.0E+15 ohms
Volume resistivity	IEC 60093	>1.0E+13 ohms·cm
Compared to the Leakage Tracking Index (CTI)	IEC 60112	PLC 3

Thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature (HDT)		ISO 75-2/Af	198 °C
vicat		ISO 306/A50	218 °C
vicat	vicat		ISO 306/B50	190 °C
Hot deformation temperature (HDT)		ISO 75-2/Bf	219 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.