Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 1.2到1.3 % |
| density | | ASTM D792 | 1.11 g/cm³ |
| Shrinkage rate | Flow | | 1.2 到 1.3 % |
| density | | ASTMD792 | 1.11 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 95 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 95 |
| tensile strength | | ASTM D638 | 29.4 MPa |
| elongation | Break | ASTM D638 | 20 % |
| Flexural modulus | | ASTM D790 | 2260 MPa |
| bending strength | | ASTM D790 | 53.9 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | 39 J/m |
| tensile strength | | ASTMD638 | 29.4 MPa |
| elongation | Break | ASTMD638 | 20 % |
| Flexural modulus | | ASTMD790 | 2260 MPa |
| bending strength | | ASTMD790 | 53.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 39 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D648 | 143 ℃ |
| | ASTM D648 | 90.0 ℃ |
| melting temperature | | DSC | 163 ℃ |
| UL flame retardant rating | | UL 94 | V-2 |
| | ASTMD648 | 90.0 °C |
| melting temperature | | DSC | 163 °C |
| | ASTMD648 | 143 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.