Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 2.1 g/10min |
| Resistance to environmental stress cracking | | ASTMD1693 | >1000 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 54 |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 低温热封性、高速成型性 |
| purpose | | | 复合膜、工业用膜 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 2.1 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 17.0 Mpa |
| Tensile strain | | ISO527-2 | 350 % |
| Flexural modulus | | ISO178 | 220 Mpa |
| Shore hardness | | ISO 868 | 54 |
| Tensile fracture strain | | ISO 527-2 | 350 % |
| Shear supported beam without notch impact strength | | ISO 179 | No Break |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 无断裂 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 915 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 2.1 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306 | 93.0 °C |
| melting temperature | | ISO11357-3 | 116 °C |
| vicat | | ISO 306 | 93 ℃ |
| melt mass-flow rate | | ISO 11357-3 | 116 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.